Supported membrane

ABSTRACT

A supported membrane comprising a non-woven monofiliment support layer wherein dense membranes with a maximum width of 5000 μm are surrounded by filaments. The invention further relates to a process for the preparation of said supported membranes.

FIELD OF THE INVENTION

The invention relates to a supported membrane and a process for itspreparation.

BACKGROUND OF THE INVENTION

It is known to form membranes in the aperture of a loop or a series ofloops with opening widths of 2.5-7.5 cm, or between at least twosubstantially parallel filaments spaced at a distance of less than 2.5cm to define elongated apertures having lengths which greatly exceed thedistance between said filaments. The resulting membranes each have asubstantial surface area which is free of support material and are quitevulnerable to rupture caused by the pressure differences applied acrosssuch membranes in reverse osmosis processes.

It is further known to use woven cloth as support for membranes having athickness substantially equal to the cloth which is twice the thicknessof the yarns forming the cloth at crossover points in the cloth weave.Due to said membrane thickness the flux of a permeable compound throughthe membrane will be unacceptably low in many cases.

For many applications it would be desirable to have at one's disposaldense (i.e. non-porous) thin membranes (permitting high rates of flowtherethrough) which possess sufficient strength to be applied inindustrial separation processes.

It has now been found that excellent supported membranes can be providedby locating dense membranes in the openings of a non-woven monofilamentsupport layer.

SUMMARY OF THE INVENTION

The invention therefore relates to a supported membrane comprising anon-woven monofilament support layer wherein dense membranes having amaximum width of about 5000 μm are surrounded by the filaments of thesupport layer.

The invention further relates to a process for preparing a supportedmembrane which comprises coating a non-woven monofilament support layerwith a solution comprising a (pre) polymer in a suitable solvent,removing at least part of the solvent from the coated layer and allowingdense membranes to be formed in areas surrounded by monofilaments.

DETAILED DESCRIPTION OF THE INVENTION

The dense membranes suitably have a width from 5-2000 μm, and preferablyfrom 5-500 μm for most applications. Membranes which have a width ofmore than 5000 μm between opposite filaments of the support layer willtend to rupture even at a small pressure difference between the twosides of such a membrane, unless the membrane thickness is considerablewhich is undesirable for most applications.

The thickness of the dense membranes present in the supporting membraneaccording to the invention is less than their width and suitably lessthan the thickness of the filaments; preferably the thickness of thedense membranes is less than 25 μm, most preferably less than 10 μm.

Although very small membranes (having a width of e.g. less than 5 μm)can usually withstand high pressure differences (e.g. above 100 bar)between both sides, even when their thickness is only a few μm, theirsurface area is usually less than 5 percent of the total surface area ofthe supported membrane which is too low for most applications.

The support layer may comprise any type of non-woven monofilaments whichpossess sufficient strength and regularity (thickness and surfacesmoothness) provided that the monofilaments are substantiallynon-soluble in the membrane-forming compound itself and in suitablesolvents for said compound. Moreover, the monofilaments shouldpreferably be compatible with (pre) polymer solutions which are suitablyused to form the dense membranes in the supported membranes according tothe invention, in order to attain a substantially complete coating ofthe monofilaments by said solutions.

Suitable non-woven monofilament support layers comprise a polymeric-,glass fiber- and/or metallic (e.g. steel) mesh; a preferred combinationof said materials is a polymer-coated steel mesh having openings ofsubstantially equal size. Preferred polymeric compounds includepolyesters, such as DACRON and TERYLENE; polyalkylenes which maycomprise halogen moieties, such as polytetrafluoroethylene, andcellulose derivatives (e.g. cellulose acetate or nitro cellulose).

A main advantage of the supported membranes according to the invention,compared with membranes comprising a porous supporting layer extendingover the surface of a dense membrane layer, is the possibility tomaintain fluid flows directly along both sides of the dense membraneswhich are now located in the support, thereby substantially reducing oreven eliminating concentration polarization in the fluid layers adjacentto the membrane surfaces. Consequently, the supported membranesaccording to the invention can be advantageously applied in dialysisprocesses wherein the concentration gradient in a plane perpendicular tothe membrane surface provides the driving force for the transport of aparticular compound through the membrane. Furthermore, said supportedmembranes are excellently suited for application in reverse osmosisprocesses due to their inherent strength, in particular when the densemembranes have a width from 5-100 μm, which makes it possible tomaintain pressure differences of more than 10 bar, or even 100 bar,between both sides of the membranes.

The supported membranes according to the invention may be used in anyconfiguration known in the art e.g. in the form of flat sheets;preferably, the supported membranes are spirally wound in such a mannerthat a fluid flow can be maintained along both sides of the densemembranes. Spacers, such as a mesh, a perforated sheet or a porouslayer, may be applied between the supported membranes in spirally woundmodules.

A wide variety of (pre) polymers can be applied for the dense membraneswhich are present in the supported membrane according to the invention.The applied polymers may either comprise thermoplastics, such aspolyalkylenes (in particular polypropylene) or thermo-hardeningcompounds, such as (silicone) rubbers, resins or fluoro-elastomers (e.g.polydimethyl siloxane, polyurethane, styrene-butadiene-styrene rubber orfluoro silicone elastomer).

In order to obtain substantially hole-free supported membranes, it isimportant that a good wetting of the monofilaments is effected by the(pre) polymer solution. Depending on the combination of monofilamentmaterial and polymer solution, treatment of the support layer with asurface active agent such as stearinic acid or polyisobutylene maleicacid anhydride triethylene pentaacetate before coating with the (pre)polymer solution can be advantageous.

Alternatively, a surface active agent can be suitably added to thepolymer solution.

The concentration of (pre) polymer in the polymer solution may be chosenwithin a wide range, suitably within a range from 1-50% by weight ofpolymer in solvent, depending on the types of polymer and solventapplied. In case the surface tension of the polymer solution isrelatively high, it can be advantageous to use a relatively concentratedpolymer solution in order to prevent the formation of holes in the areasof the coated support layer where dense membranes are to be formed. Forinstance, in case a solution of polypropylene in a solvent withrelatively high viscosity and boiling point (e.g. decaline) is applied,the concentration of polypropylene in said solvent is preferably atleast 5% by weight.

The support layer may be coated e.g. by submerging the layer in thepolymer solution or by spraying polymer solution on the layer which isthen suitably supported by solid or liquid supporting means.

Solvent is suitably removed, after coating for the support layer withthe polymer solution, by evaporation, preferably at an elevatedtemperature. In some cases it is possible to remove at least part of thesolvent by placing the coated support layer on or in a body of liquidwherein the solvent is soluble and wherein the polymer coating isinsoluble.

Preferably, solvent is removed from the coated support layer at anelevated temperature at which no phase separation occurs in the (pre)polymer coating from which the dense membranes are to be formed. Inparticular when a polypropylene solution is used for preparing densemembranes therefrom, it is important that the temperature should notfall below 120° C., and preferably not below 140° C., during coating ofthe support layer and during the subsequent evaporation step, in orderto avoid crystallization of polypropylene which would give rise tounacceptable pore formation in the membranes thus formed.

After having removed at least part, and preferably substantially all ofthe solvent from the coated supporting layer, a further heat treatmentmay be applied in particular when thermo-hardening polymers are used,suitably in combination with catalysts and/or cross-linking agents, inthe coating. Suitably, the heat treatment is carried out at atemperature from 100°-160° C for a period of 30 minutes-24 hours.

The invention will be further illustrated by means of the followingExamples.

EXAMPLE 1

A non-woven monofilament polyester mesh comprising openings having awidth of 49 μm was, after cleaning with n-hexane, submerged at atemperature of 20° C. in a solution comprising 2.5% by weight of astyrene/butadiene/styrene block copolymer dissolved in cyclohexane,dried at 50° C. and again submersed in said solution and dried at 50° C.The resulting supported membrane contained 18 g copolymer/m² mesh,permitting a carbon dioxide gas flux of 120 m³ (S.T.P.)/bar, m², daythrough the dense membranes formed in the mesh openings.

EXAMPLE 2

A similar cleaned polyester mesh as described in Example 1 was submergedin a solution comprising 5% by weight of polypropylene and 1% by weightof stearinic acid in decalin at a temperature of 150° C. which wasmaintained during drying of the coated mesh. Accordingly, densemembranes were obtained which covered 20% of the total supportedmembrane area, the remaining area being covered by the monofilaments ofthe mesh; the coating amounted to 14 g polypropylene/m² mesh.

In dialysis experiments carried out with the supported dense membrane ata temperature of 55° C., a flux of n-hexane and n-octane amounting to0.41 and 1.27 m³ /m², day, respectively, was obtained.

EXAMPLE 3

A steel mesh comprising openings having a width of 2 mm was cleaned withn-hexane and then submerged in a polypropylene-comprising solution asdescribed in Example 2. During drying at 150° C. of the steel meshcoated with 23 g polypropylene/m² mesh dense membranes were formed whichcovered 80% of the total surface area of the supported membrane.

In dialysis experiments carried out with said supported membrane at atemperature of 55° C., fluxes of n-hexane and iso-octane amounting to0.30 and 0.14 m³ /m², day, respectively, were obtained.

EXAMPLE 4

A polytetrafluoroethylene mesh having openings with a width of 50 μm wascleaned with n-hexane and subsequently submerged in a solutioncomprising 2.5% by weight of poly dimethyl siloxane and 1% by weight ofpolyisobutylene maleic acid anhydride triethylene pentaacetate inisooctane, dried at 50° C. and cured at 120° C. for 4 hours.

The resulting supported membrane showed excellent adhesion between thecoating and the mesh after wetting with n-hexane.

What is claimed is:
 1. A supported membrane comprising a dense hole-freemembrane supported on a non-woven monofilament support layer wherein thedense membrane is a polymer selected from the group consisting ofpolyalkylene, polydimethyl siloxane, polyurethane, andstyrene-butadiene-styrene rubber, wherein the dense membrane has amaximum width of about 5000 μm and a thickness less than about 25 μm andthe dense membrane is surrounded by the filaments of the support layer.2. The supported membrane of claim 1 wherein the dense membranes have awidth from about 5 to 2000 μm.
 3. The supported membrane of claim 1wherein the dense membranes have a width from about 5 to about 500 μm.4. The supported membrane of claim 3 wherein the dense membranes have athickness less than about 10 μm.
 5. The supported membrane of claim 1wherein the non-woven monofilament support layer comprises a meshselected from the group consisting of a polymeric mesh, a glass fibermesh, a metallic mesh and any combination of polymeric, glass fiber andmetallic mesh.
 6. The supported membrane of claim 5 wherein thenon-woven monofilament support layer comprises a mesh selected from thegroup consisting of a polyester mesh, a steel mesh, and apolytetrafluoroethylene mesh.
 7. The supported membrane of claim 1wherein the dense membranes comprise a non-porous polyalkylene.
 8. Thesupported membrane of claim 7 wherein the dense membranes comprise anon-porous polypropylene.
 9. The supported membrane of claim 1 whereinthe non-woven monofilament support layer is comprised of a polyestermesh and the dense membranes are comprised of astyrene-butadiene-styrene block copolymer.
 10. The supported membrane ofclaim 1 wherein the non-woven monofilament support layer is comprised ofa polytetrafluoroethylene mesh and the dense membranes are comprised ofpoly dimethyl siloxane.
 11. The supported membrane of claim 1 whereinthe supported membrane is spirally wound such that along both sides ofthe supported membrane a fluid flow can be maintained.